DIN1.2311 P20 Plastic Mould Steel

• Customization: Available
• Type: Round
• Standard: AISI, ASTM, DIN
• Model NO.: DIN1.2311 P20
• Composition: Ferrous Steel Scrap
• Technique: Hot Forged or Hot Rolled
• Shape: Round,Flat or Square
• Surface Treatment: Black Surface, Grinded,Peeled,Milled,Polished
• Special Use: Mold Steel
• Application: Die Steel Bar
• Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
• Smelting Process: Ef, Eaf, ESR
• Delivery Condition: Hot Rolled, Forged, Annealed,Quenched and Tempered
• Surface Condition: Black Surface, Grinded,Peeled,Milled,Polished
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: FUSHUN
• Origin: Huangshi, Hubei
• HS Code: 7228100000
• Production Capacity: 5000tons/Year

Product Description

Introduction

Low-carbon mold steels or group P steels are of different types that include P2, P3, P4, P5, P6, P20, and P21 mould steel. Chromium and nickel are the main alloying elements found in group P steels.
P20 plastic mould steel are nitrided or carburized. These steels are capable of being machined into complex and large dies and molds. P20 plastic mould steel are mostly used in the carburized condition.

Applications

P20 plastic mould steel is ideally suited for the production of plastic moulds. Typical applications include die holders, zinc die casting dies, backers, bolsters and injection moulds. The versatility of P20 plastic mould steel with its high tensile characteristics enables uses for a variety of other applications such as shafts, rails and wear strips

Quality Standard

ASTM A681 - 08 Standard Specification for Tool Steels Alloy.

All Grades Comparison

ASTM A681	Werkstoff
P20	1.2311

Chemical Composition(%)

C	Si	Mn	P	S	Cr	Mo
0.28-0.40	0.10-0.50	0.20-0.80	0.030 max	0.030 max	1.40-2.00	0.30-0.55

Mechanical Properties

Properties	Metric
Hardness, Brinell (typical)	300
Hardness, Rockwell C (typical)	30
Tensile strength	965-1030 MPa
Yield Strength	827-862 MPa
Elongation at break (in 50 mm (2″))	20.0% min
Compressive strength	862 MPa
Charpy impact (V-Notch)	27.1-33.9 J

HEAT TREATMENT

Forging: P20 plastic mould steel are forged at 1093°C (2000°F) down to 899°C (1650°F). Forging below 871°C (1600°F) is not recommended for these steels.
Annealing: Annealing takes place at 760-788°C (1400 to 1450°F) and then the steels are cooled slowly in the furnace at a temperature less than 4°C (40°F) per hour.
Stress Relieving: When dies are heavily machined, we recommend stabilising just before finish machining in order to relieve machining strains. Heat to 460-500°C. Soak well and allow to cool in the air.
Hardening: Heat the steel uniformly to 820-840°C until heated through. Quench in oil.
Tempering: Heat uniformly and soak at the tempering temperature for at least one hour per 25mm of section. Allow to cool in still air.
Carburising / Case Hardening: Tools produced from may be case hardened, which can achieve a surface hardness of 55 to 59 HRc.
Tufftriding: At 570°C tufftriding of P20 tool steel will give a surface hardness of approximately 700HV. Allowing two hours treatment the surface hard layer will be approximately 0.1mm.
Hard Chromium Plating: To avoid hydrogen embrittlement P20 should be tempered for 4 hours at 180°C for 4 hours after hard chromium plating
Flame / Induction Hardening: Flame or induction hardening of P20 will achieve a hardness of 50 to 55HRc. Air cooling is preferable, though smaller components may require forced cooling. Temper immediately after hardening.
Cold Working:P20 plastic mould steel are capable of being readily cold worked by using conventional tooling methods with the alloy in the annealed condition.
Welding: Conventional methods are used for welding of P20 plastic mould steel.
Forming: P20 plastic mould steel can be readily formed by conventional methods in the annealed condition.
Machinability: P20 plastic mould steel have excellent machinability at about 80% that of water hardening steels.

Mill′s test certificate

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.