Stainless Steel - Grade 317 (UNS S31700)

• Customization: Available
• Type: Stainless Steel Bars
• Standard: ASTM
• Model NO.: 317
• Certification: ISO
• Shape: Round, Square, Flat
• Technique: Hot Rolled, Forged
• Surface Treatment: Grinded, Peeled, Polished, Rough Turned
• Similar Grades: Uns S31700
• Size Range: Diameter: 20-480mm
• Delivery Condition: Annealed, Qunched and Tempered
• Surface Condition: Grinded, Peeled, Polished, Rough Turned
• Quality Standard: ASTM-A276
• Transport Package: Apply The Shipping Packing
• Specification: Diameter: 20-480mm
• Trademark: CHENGQUAN
• Origin: Hubei, Huangshi
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

Similar Grades:
 UNS S31700
Shape: 
Round, Flat, Square.
Size Range:

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	20-480	-	-	2000-5800
Square	20-480	-	-	2000-5800
flat	-	20-50	80-600	2000-5800

 
Steel-making Condition: 
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:

C	Mn	P	S	Si	Cr	Ni	N	Mo
0.08max	2.00max	0.045max	0.030max	1.0max	18.0-20.0	11.0-15.0	0.10max	3.0-4.0

 
 
Mechanical Properties
The mechanical properties of annealed grade 317 stainless steel are displayed in the following table.

Properties	Metric	Imperial
Tensile strength	620 MPa	89900 psi
Yield strength	275 MPa	39900 psi
Elastic modulus	193 GPa	27993 ksi
Poisson's ratio	0.27-0.30	0.27-0.30
Elongation at break (in 50 mm)	45%	45%
Hardness, Rockwell B	85	85

 
 
Fabrication and Heat Treatment
Machinability
Grade 317 stainless steel is tougher than 304 stainless steel. It is recommended to use chip breakers. Hardenability of this alloy will be reduced if constant feeds and low speeds are used.
Welding
Grade 317 stainless steel can be welded using fusion and resistance methods. Oxyacetylene welding method is not preferred for this alloy. AWS E/ER317 or 317L filler metal can be used to obtain good result.
Hot Working
Grade 317 stainless steel can be hot worked using all common hot working procedures. It is heated at 1149-1260C (2100-2300F). It should not be heated below 927C (1700F). Post-work annealing can be done to retain the corrosion resistance property.
Cold Working
Stamping, shearing, drawing, and heading can be done successfully. Post-work annealing is performed in order to reduce internal stress.
Annealing
Grade 317 stainless steel is annealed at 1010-1121C (1850-2050F) followed by cooling.
Hardening
Grade 317 stainless steel does not react to heat treatment. It can be hardened by cold working.
Applications
Grade 317 stainless steel is used in the following applications:
· Pulping paper
· Textile
· Chemical equipment
 
Introduction
Stainless steels are known as high-alloy steels. They consist about 4-30% of chromium. They are classified into martensitic, austenitic, and ferritic steels based on their crystalline structure.
Grade 317 stainless steel is a modified version of 316 stainless steel. It has high strength and corrosion resistance. The following datasheet gives more details about grade 317 stainless steel.
 