DIN1.7380 10crmo9-10 ASTM A182 F22 Stainless Steel for High Temperature

• Customization: Available
• Type: Stainless Steel Bars
• Standard: ASTM, DIN, EN
• Model NO.: DIN1.7380 10CrMo9-10 ASTM A182 F22
• Grade: DIN1.7380 10crmo9-10 ASTM A182 F22
• Certification: ISO
• Shape: Round
• Technique: Hot Rolled
• Surface Treatment: Polished
• Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
• Smelting Process: Ef, Eaf, ESR
• Delivery Condition: Hot Rolled, Forged, Annealed, Qt
• Surface Condition: Black Surface, Grinded, Peeled, Milled, Polished
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: CHENGQUAN
• Origin: Huangshi, Hubei
• HS Code: 7228600000
• Production Capacity: 5000tons/Year

Product Description

Application

F22 stainless steel is a low alloy steel containing nominally 2.25% Chromium. This F22 stainless steel is widely used in the oil patch wellhead applications for connectors, hangers and block valves. Hardness levels up to 22 HRC are approved to NACE MR0175. The grade is often used as the base metal for clad components. If supplied to ASTM A182 in the normalised and tempered condition, the 0.2% Proof Stress minimum is 30 KSI.

All Grades Comparison

Material no.	DIN	ASTM
1.7380	10CrMo9-10	F22

Quality Standard

ASTM A182 Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service

Chemical Composition(%)

C	Mn	Si	P	S	Cr	Mo
0.05-0.15	0.30-0.60	0.50 max	0.040 max	0.040 max	2.00-2.50	0.87-1.13

Mechanical Properties(T=20°C)

Delivery Condition	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation(%)	Reduction Ratio(%)	Hardness (HB)
Normalized and Tempered	900 min	675 min	/	/	/
Slow Cooling	415 min	205 min	20 min	35 min	170 max

HEAT TREATMENT

Normalizing: Temperature: 920°-980°C.
Stress Relieving: Stree relieving to remove maching stresses should be carried out by heating to 675°C, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Austenization: Temperature:920°-980°C
Tempering: Tempering temperature: 650°-750°C