1.4545 Uns S15500 Xm-12 Precipitation Hardening Stainless Steel

• Customization: Available
• Type: Stainless Steel Flats
• Standard: ASTM, DIN
• Model NO.: 1.4545 UNS S15500 XM-12 15-5PH
• Grade: 1.4545 Uns S15500 Xm-12 15-5pH
• Certification: ISO
• Shape: Flat
• Technique: Hot Rolled
• Surface Treatment: Bright
• Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
• Smelting Process: Ef, Eaf, ESR
• Delivery Condition: Hot Rolled, Forged, Annealed,Quenched and Tempered
• MOQ: 500kgs
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: CHENGQUAN
• Origin: Huangshi, Hubei
• HS Code: 7228600000
• Production Capacity: 5000tons/Year

Product Description

Similar Grade:

DIN	ASTM	UNS	CNU
1.4545	XM-12	S15500	15-5PH

Chemical Composition(%)

C	Si	Mn	P	S	Cr	Ni	Cu	Nb+Ta
0.07 max	1.0 max	1.0 max	0.030 max	0.035 max	14.0-15.0	3.5-5.5	2.5-4.5	0.15-0.45

Mechanical Properties

Delivery Condition	Modulus of Elasticity (GPa)	Modulus of Rigidity (GPa)	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2(Mpa)	Elongation % in 2″ (50.8 mm)	Reduction Of Area  (%)	Hardness  (HRC)
A(annealed)	/	/	/	/	/	/	35 max
H 900	197.6	77.3	1378 min	1276 min	14 min	50 min	44 min
H925	/	/	1309 min	1207 min	14 min	54 min	42 min
H1025	/	75.9	1173 min	1138 min	15 min	56 min	38 min
H1075	/	69	1138 min	1035 min	16 min	58 min	36 min
H1100	/	/	1035 min	931 min	17 min	58 min	34 min
H1150	/	69	1000 min	862 min	19 min	60 min	33 min

Mill′s test certificate:
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
Quality Standard:
ASTM A564 2004 Standard Specification for Hot Rolled and Cold Finished Age Hardening Stainless Steel Bars and Shapes
ASTM A705 Standard Specification for Age Hardening Stainless Steel Forgings

Introduction:
15-5PH is a martensitic precipitation-hardening stainless steel that provides high strength, good
corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C) and good toughness in both the longitudinal and transverse directions in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling.
15-5PH is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in the
aerospace, chemical, petrochemical, food processing, paper and general metalworking industries.

Applications:
Aircraft components
High pressure corrosive fabricated parts such as valves
Shafts
Fasteners
Fittings and gears