20nicrmo2-2 DIN1.6523 Sncm220 8620 Gear Steel

• Customization: Available
• Type: Flat
• Standard: AISI, ASTM, DIN, JIS
• Model NO.: 20NiCrMo2-2 DIN1.6523 SNCM220 8620
• Composition: Ferrous Steel Scrap
• Shape: Round,Flat or Square
• Surface Treatment: Black Surface,Grinded or Peeled
• Special Use: Gear Steel
• Application: Structural Steel Bar
• Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
• Smelting Process: Ef, Eaf, ESR
• Delivery Condition: Hot Rolled, Forged, Annealed,Quenched and Tempered
• Surface Condition: Black Surface, Grinded,Peeled,Milled,Polished
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: CHENGQUAN
• Origin: Huangshi, Hubei
• HS Code: 7228600000
• Production Capacity: 5000tons/Year

Product Description

Characteristics

8620 gear steel is a low carbon nickel chromium molybdenum alloy steel. And it is a low cost steel with good carburized properties. The nickel content contributes to case toughness at high strength with above average core toughness. The chromium and molybdenum support the proper formation of carbides resulting in good surface hardness and wear. It is the most widely used carburizing alloy.

Applications:

When hardened and formed,8620 gear steel may be used to produce hard wearing machine parts in a wide variety of industries. With its combination of elements along with the ease with which it may be processed, 8620 gear steels a good choice for a variety of applications. Carburized 8620 gear steel is strong and durable and as a result is preferred in certain manufacturing applications. It is used to make a wide range of gears, crankshafts, gear rings, pinions, piston pins, cams, gauges, tie bars, collets, bushings and bolting as well as hand tools and a multitude of machinery parts and components. Structural parts such as gears, pinions, spline shafts, pins and a variety of other important applications requiring a hard wear surface and a ductile core.

Quality Standard:

ASTM A29 Standard Specification Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements
EN 10277 Bright steel products.
EN 10278 Dimensions and tolerances of bright steel products

All Grades Comparison:

DIN	ASTM	JIS	EN
1.6523	8620	SNCM220	20NiCrMo2-2

Chemical Composition(%):

Steel Grade	C	Mn	Si	P	S	Cr	Ni	Mo
8620	0.18-0.23	0.70-0.90	0.15-0.35	0.030 max	0.040 max	0.40-0.60	0.40-0.70	0.15-0.25
20NiCrMo2-2	0.17-0.23	0.65-0.95	0.40 max	0.030 max	0.030 max	0.35-0.70	0.40-0.70	0.15-0.25
SNCM220	0.18-0.23	0.60-0.90	0.15-0.35	0.030 max	0.040 max	0.40-0.65	0.40-0.70	0.15-0.30

Mechanical Properties( T=20°C if not differently stated ):

Dia(mm)	Tensile Strength Rm (Mpa)	Yield Strength R2 (Mpa)	Fracture elongation A5 (%)	Hardness (HB)
18-40	925 min	690 min	17 min	275 max
40-80	740 min	493 min	20 min	220 max

Heat Treatment:

This 8620 gear steel may be hardened by heating to 1500°F followed by a water quench. Carburize at 1650°F to 1700°F in an appropriate carburizing medium and oil quench to harden. Improved carburized case and core properties can be obtained by furnace cooling from carburizing at 1650°F-1700°F and then reheating to 1575°F.
Annealing:
8620 gear steel may be given a full anneal at 1550°F and slow cooling at not more than 50°F per hour down to 850°F. From there it may be air cooled.
Hardening:
Hardening is done by oil quench from 1675°F. Carburizing is accomplished at the same 1650°F-1700°F range in a carburizing "pack" or environment, followed by oil quench for thin sections or a furnace cool for heavier (over 3/4'' sections. Following carburizing of heavy sections a reheat at 1575°F will enhance both case and core properties of the alloy.
Tempering:
Tempering of carburized parts is done at 250°F-300°F and this will result in the alloy having a core strength of approximately 135 ksi minimum with Rockwell C case hardness of 90. Tempering of heat treated and water quenched parts (not carburized) is done at 400°F-1300°F with greater hardness the lower the tempering temperature.

Machinability:

Machining is done prior to carburizing to within as close a tolerance as possible. Finish machining, after heat treatment and/or carburizing, should be at a minimum so as not to impair the hardened case of the part. Machining may be done by conventional means prior to heat treatment -after carburizing machining is usually limited to grinding.

Forming:

Forming characteristics of 8620 gear steel are good in the annealed condition.

Welding:

The 8620 gear steel may be welded by conventional methods, usually gas or arc welding. Preheating at 400°F is beneficial and subsequent heating after welding is recommended -consult the approved weld procedure for the method used.

Forging:

The alloy may be forged at 2200°F down to 1800°F prior to the hardening heat treatment or carburizing.

Hot Working:

Hot working may be accomplished prior to hardening or carburizing. Consult the alloy supplier for information as to temperatures.

Cold Working:

The alloy may be cold worked in the annealed condition by conventional methods. Cold working, as with machining, should be done to as close a tolerance as possible before heat treatment or carburizing.