AISI3415 AMS6260e 655h13 15nicr13 1.5752 Case Hardening Steel

• Customization: Available
• Type: Flat
• Standard: AISI, ASTM, DIN, JIS, BS
• Model NO.: AISI3415 AMS6260E 655H13 15NiCr13 1.5752
• Composition: Ferrous Steel Scrap
• Technique: Hot Forged or Hot Rolled
• Shape: Round, Flat or Square
• Surface Treatment: Black Surface, Grinded, Peeled, Milled, Polished
• Special Use: Alloy Structural Steel
• Application: Structural Steel Bar
• Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
• Smelting Process: Ef, Eaf, ESR
• Delivery Condition: Hot Rolled, Forged, Annealed, Quenched and Tempered
• Surface Condition: Black Surface, Grinded, Peeled, Milled, Polished
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: CHENGQUAN
• Origin: Huangshi, Hubei
• HS Code: 7228100000
• Production Capacity: 5000tons/Year

Product Description

Description

15NiCr13 is a remelted nickel chrome molybdenum case hardening steel produced by the PESR* (Pressurised ESR) method designed for components with high demand in toughness and core strength.

Application

Highly stressed components in automotive construction, and for general engineering purposes, e. g. gears, crankshafts, gearshafts.

Advantages

Good machinability (hobbing and turning).
Good dimensional stability.
Homogenous PESR structure suitable for the production of large components.
Improved polishability, photo-etchability and EDM due to higher purity.
Suitable for single and double hardening.

All Grades Comparison

DIN	EN	ANFOR	BS	GOST	AISI	AMS	UNI
1.5752	15NiCr13	14NC11	655H13	G55M13	3415	6260E	18NC13

Quality Standard

BS EN 10084 2008 Case hardening steels - Technical delivery conditions
BS EN 10277-4-2008 Bright steel products -Case Hardening Steel- Part 4 General

Chemical Composition(%)

C	Mn	Si	P	S	Cr	Ni
0.14-0.20	0.40-0.70	0.40 max	0.025 max	0.035 max	0.60-0.90	3.00-3.50

Mechanical Properties(T=20°C if not differently stated)

Process	Diameter(mm)	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation A5 (%)	Area Reduction Ratio C (%)	Hardness (HB)
SOFT ANNEALED	/	/	/	/	/	255 max
Treated to hardness range	/	/	/	/	/	179-229
Treated to ferrite-pearlite structure	/	/	/	/	166-217
QUENCHED AND TEMPERED	11 max	1030-1320	835 min	9 min	40 min	/
QUENCHED AND TEMPERED	11-30	930-1230	785 min	10 min	45 min	/
QUENCHED AND TEMPERED	30-63	880-1180	735 min	10 min	45 min	/

HEAT TREATMENT:

Process	Temperature(°C)
End quench test Austenitizing	880 min
Carburizing	880-980
Core-hardening	840-880
Case-hardening	780-820
Tempering	150-200	/

Mill′s test certificate:

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.