DIN 1.3265, T5, S18-1-2-10, SKH4 High Speed Steel
Similar Grade: DIN 1.3265, T5, S18-1-2-10, SKH4
Shape: Round, Flat, Square.
Size Range:
| |
Diameter(mm) |
Thickness (mm) |
Width (mm) |
Length(mm) |
| Round |
10-420 |
- |
- |
2000-5800 |
| Square |
- |
1-300 |
- |
2000-5800 |
| flat |
- |
1-300 |
50-600 |
2000-5800 |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details |
In seaworthy packing, as your requirement. |
| Delivery details |
within 30-50 days |
Chemical Composition:
| Grade |
C |
Mn |
P |
S |
Si |
Cr |
Mo |
W |
V |
Co |
| 1.3265 |
0.72
-0.80 |
0.40 Max |
0.45
Max |
0.03 Max |
0.03
Max |
3.80-
4.50 |
0.50
-0.80 |
17.50-
18.50 |
1.40-
1.70 |
9.00-
10.00 |
Heat Treatment:
1. Preheat din 1.3265 steel slowly to the temperature of 820-870°C;
2. Heating up to quenching temperature of 1270-1290°C;
3. Make sure that the material is heated throughly;
4. Quench in the oil or brine;
5. Heat uniformly to the required tempering temperature;
6. Withdraw S18-1-2-10 steel from the furnace and cool in air;
7. The general tempering temperature is 540-560°C which makes the material 63HRC.
8. The 1.3265 tool steel is also suitable for vacuum hardening and triple tempering is strongly recommended.
Product Introduction:
High speed steel