DIN 1.5918 17crni6-6 Engineering Steel Bar with Good Quality

• Customization: Available
• Type: Alloy Steel Bar
• Standard: ASTM, DIN
• Model NO.: DIN1.5918 17CrNi6-6
• Composition: Ferrous Steel Scrap
• Technique: Forged Rolled
• Shape: Round Flat
• Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
• Special Use: Mold Steel
• Application: Structural Steel Bar
• Size Range: 20-480 mm
• Quality Standard: BS En ISO 4957
• Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
• MOQ: 1t
• Transport Package: Seaworthy Packing
• Specification: DIN1.5918 17CrNi6-6
• Trademark: FUSHUN
• Origin: , China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

DIN1.5918 17CrNi6-6 Engineering Steel

Similar Grade: DIN1.5918 17CrNi6-6

Shape: Round, Flat, Square.

Size Range:

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	20-420	-	-	2000-5800
Square	20-420	-	-	2000-5800
flat	-	20-50	50-600	2000-5800

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:

Grade	C	Mn	P	S	Si	Cr	Ni
1.5918	0.14- 0.20	0.50- 0.80	0.025 max	0.035 max	0.40 max	1.40- 1.70	1.40- 1.70

 
 
 

Mechanical Properties:

Process	Diameter(mm)	Tensile Strength Rm (Mpa)	Hardness (HB)
Treated to improve shearability	/	/	255 max
SOFT ANNEALED	/	/	229 max
Treated for strength	/	/	175-229
Treated for ferrite and pearlite structure and hardness range	/	/	156-207
QUENCHED AND TEMPERED	16 max	1200 min	/
QUENCHED AND TEMPERED	16-40	1100 min	/
QUENCHED AND TEMPERED	40-100	900 min	/

 
Heat Treatment and Fabrication:

 
 
 
 
 
 

Process	Temperature(oC)	Media
Forging or hot rolling	1100-850	/
Normalising	850-880	air
Soft annealing	650-700	furnace
Carburising	880-980	/
Core hardening	830-870	oil
Intermediate annealing	630-650	/
Case hardening	780-820	oil
Tempering	150-200	/

 

Applications:
Alloyed case hardening steel for highly strained parts and good toughness at core tensile strength of 900 - 1200 N/mm². Driving bevel gears, crown wheels, gears, shafts, bolts for automotive and gear components.
Introduction:
Structural, pressure vessel and engineering steels.
 