DIN1.4542 Precipitation Hardening Martensitic Stainless Steel

• Customization: Available
• Type: Stainless Steel Bars
• Standard: AISI, JIS, DIN, EN
• Model NO.: DIN1.4542, UNS S17400, 630, 17-4PH
• Grade: High Quality Steel
• Certification: ISO
• Shape: Round, Flat, Square.
• Technique: Forged, Rolled
• Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
• Size Range: 50-420mm
• Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
• Surface Condition: Black, Grinded, Peeled, Rough Turned, Polished
• Delivery Condition: Annealed, Quenched + Tempered
• MOQ: 1t
• Transport Package: Seaworthy Packing
• Specification: DIN1.4542, UNS S17400, 630, 17-4PH
• Trademark: Chengquan
• Origin: Huangshi, China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

DIN1.4542 Precipitation Hardening Martensitic Stainless Steel
 
Similar Grade: DIN1.4542, UNS S17400, 630, 17-4PH, X5CrNiCuNb 16-4
 
Shape: round, flat, square.
 
Size Range:
 

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	50-420	-	-	2000-5800
Square	50-420	-	-	2000-5800
flat	-	20-50	80-600	2000-5800

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished
 
Features:
1. Competitive price
2. Immediate delivery
3. Premium quality
4. Reliable service
 
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:
 

Grade	C	Mn	P	S	Si	Cr	Ni	Cu	Nb
1.4542	0.07 max	1.0 max	0.030max	0.035 max	1.0 max	15.5- 17.5	3.0- 5.0	3.0- 5.0	0.15- 0.45

 
Heat Treatment:
Solution treatment (Condition A): Grade 630 stainless steels are heated at 1040°C for 0.5 h, then air-cooled to 30°C. Small sections of these grades can be oil quenched.
Cold Working: Alloy 17-4PH has limited cold forming properties. Cold forming can only be undertaken on plates in the fully annealed condition. Stress corrosion resistance is enhanced by re-aging at the precipitation hardening temperature after cold working.
Hot Forming: Heat uniformly at 1742-2192°F (950-1200°C). A full solution anneal, cooling lower than 76°F (25°C) and aging at the required temperature must occur after hot forming. The post forming heat treatment should be a function of the desired mechanical properties.
Annealing: 440C stainless steel is annealed at 843-871°C (1550-1600°F) followed by slowly cooling in the furnace.
Hardening: Grade 630 stainless steels are age-hardened at low temperatures to achieve the required mechanical properties. During the process, superficial discoloration occurs followed by shrinkage at 0.10% for condition H1150, and 0.05% for condition H900.
Welding: Alloy 17-4PH can be readily welded by most standard processes including SMAW, GTAW, PAW and GMAW.
Machinability: Alloy 17-4PH can be machined in both the solution treated and
precipitation hardened conditions. Machining characteristics may vary according to the hardness of the metal. High speed tools are acceptable, but carbide tools are preferred. Standard lubrication should be used. Dimensional changes as a result heat treatment should be taken into account if very stringent tolerances are required.

Application:
 Aerospace-structural and parts
 Biomedical-hand tools
 Chemical Processing
 Food Process Equipment
 Gate Valves
 Mechanical Components
 Nuclear Waste Processing and Storage
 Oil and Gas Production-foils, helicopter deck platforms, etc.
 Pulp and Paper-paper mill equipment
 
 
 
Product Description:
1. Alloy 1.4542 (UNS S17400), Type 630, is a chromium-nickel-copper precipitation hardening martensitic stainless steel with an addition of niobium. 17-4PH combines high strength and hardness with good corrosion resistance.
The alloy is furnished in the solution annealed condition (Condition A). It should not be used at temperatures above 572°F (300°C) or for cryogenic service. Optimal mechanical properties can be obtained by subjecting the alloy to age hardening heat treatments. Heat treatment in the 900°F (482°C) range produces the highest strength.
2. The corrosion resistance of Alloy 1.4542 is comparable to 304 stainless steel in most environments and is generally superior to the 400 series stainless steels. It is used in applications where the combination of moderate corrosion resistance and unusually high strength are required.
3. Alloy 1.4542 can be easily welded and processed by standard shop fabrication practices.