DIN1.6510 39NiCrMo3 36CrNiMo4 AISI9840 Quenched and Tempered Steel
Similar Grade: DIN1.5752 AMS6260E 655H13 15NiCr13
Shape: Round, Flat, Square.
Size Range:
| |
Diameter(mm) |
Thickness (mm) |
Width (mm) |
Length(mm) |
| Round |
20-620 |
- |
- |
2000-5800 |
| Square |
20-620 |
- |
- |
2000-5800 |
| flat |
- |
20-50 |
50-600 |
2000-5800 |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details |
In seaworthy packing, as your requirement. |
| Delivery details |
within 30-50 days |
Chemical Composition:
| Grade |
C |
Mn |
Si |
P |
S |
Cr |
Ni |
Mo |
DIN
1.6510 |
0.35-
0.43 |
0.50-
0.80 |
0.40 max |
0.025 max |
0.035 max |
0.80-
1.10 |
0.70-
1.00 |
0.15-
0.25 |
Heat Treatment and Fabrication:
| Process |
Temperature(ºC) |
| End quench test Austenitizing |
880 min |
| Carburizing |
880-980 |
| Core-hardening |
840-880 |
| Case-hardening |
780-820 |
| Tempering |
150-200 |
Product Introduction:
Good machinability (hobbing and turning).
Good dimensional stability.
Homogenous PESR structure suitable for the production of large components.
Improved polishability, photo-etchability and EDM due to higher purity.
Suitable for single and double hardening.
Contact information:
FUSHUN SPECIAL STEEL CO., LTD.
Website: fushunmetal.en.made-in-china.com
Similar Grade: DIN1.5752 AMS6260E 655H13 15NiCr13
Shape: Round, Flat, Square.
Size Range:
| |
Diameter(mm) |
Thickness (mm) |
Width (mm) |
Length(mm) |
| Round |
20-420 |
- |
- |
2000-5800 |
| Square |
20-420 |
- |
- |
2000-5800 |
| flat |
- |
20-50 |
50-600 |
2000-5800 |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details |
In seaworthy packing, as your requirement. |
| Delivery details |
within 30-50 days |
Chemical Composition:
| Grade |
C |
Mn |
P |
S |
Si |
Cr |
Ni |
| 1.5752 |
0.14-
0.20 |
0.40-
0.70 |
0.025
max |
0.035
max |
0.40
max |
0.60-
0.90 |
3.00-
3.50 |
HEAT TREATMENT:
Annealing: Austenitize at 1525ºF (830ºC) and slow cool from 1280 to 1200ºF (iso anneal) to give coarse pearlite structure for optimum machinability.
Normalizing: At 1600ºF (870ºC) followed by air cool.
Hardening: from 1525-1575ºF (830-860ºC) and oil quench for thin, intricate shapes, water quench for large, simple shapes.
Tempering: from 1000-1250ºF(540-680ºC) as per required properties.
Machinability:
this alloy may be readily machined, preferably from a coarse pearlitic structure.
Weldability:
pre-heat and post-weld stress relief are recommended for welding of this alloy. Welding should not be carried out in the hardened and tempered condition.
Application:
This steel is suited to production of highly stressed components of large cross section for aircraft, automotive and general engineering applications, such as forged propeller shafts, connecting rods, gear shafts, crankshafts and landing gear components.
Product Introduction:
This steel is suitable for different heat treatment and shows a good cold workability.