1.4000, X6Cr13, AISI410S, UNS S41008 Stainless Steel
Similar Grade: 1.4000, X6Cr13, AISI410S, UNS S41008
Shape: Round, Flat, Square.
Size Range:
Frame
Processing
Shape |
Round |
Flat |
Square |
| Thickness |
Width |
Rolling |
12-130mm |
4-150mm |
100-900mm |
-
|
Forging |
50-1000mm |
70-800mm |
300-2000mm |
70-1000mm |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details |
In seaworthy packing, as your requirement. |
| Delivery details |
within 30-50 days |
Chemical Composition:
| Grade |
C |
Mn |
P |
S |
Si |
Cr |
Ni |
N |
| 1.4000 |
0.030max |
1.50 max |
0.040 max |
0.015 max |
1.00 max |
10.50- 12.50 |
0.30- 1.00 |
0.030 max |
General properties:
corrosion resistance low
mechanical properties annealed soft
mechanical properties tempered good
Forgeability good
weldability good
machinability good
Mechnical Properties:
Density, 0.28 lbs/in3 7.73 g/cm3
Electrical Resistivity, microhm-in (microhm-cm) 68°F (21°C) - 23.7 (60) Specific Heat, BTU/lb/°F (kJ/kg?K) 32 - 212°F (0 - 100°C) - 0.11 (0.46) Thermal Conductivity, BTU/hr/ft2 /ft/°F (W/m?K) 212°F (100°C) - 15.6 (26.9) Mean Coefficient of Thermal Expansion, in/in/°F (µm/m?K) 32 - 212°F (0 - 100°C) - 6.0 x 10-6 (10.8) 32 - 600°F (0 - 315°C) - 6.4 x 10-6 (11.5) 32 -1000°F (0 - 538°C) - 6.7 x 10-6 (12.2) 32 -1200°F (0 - 649°C) - 7.5 x 10-6 (13.5) Modulus of Elasticity, ksi (MPa) 29 x 103 (200 x 103 )
Melting Range:2700 - 2790 (1482 - 1532)°F (°C)
Heat treatment:
1.4000 is not hardened by heat treatment. It is annealed in the 1600 - 1650°F (871 - 899°C) range and then air cooled, mainly to relieve cold working strains. Care should be exercised to avoid exposure at temperatures of 2000°F (1093°C) or above because of possible embrittling effects. If excessively large grains are found after annealing mildly cold-worked material, the annealing temperature should be decreased to the 1200 - 1350°F (649 - 732°C) range.
Applications:
Automotive exhaust system parts: mufflers, pipes, catalytic converters, support parts.
Constructional structures used in elevated temperatures.
Contact information:
FUSHUN SPECIAL STEEL CO., LTD.
Website: fushunmetal.en.made-in-china.com
Audited Supplier 