1.2516, 120WV4 Cold Working Tool Steel
Similar Grade:1.2516, 120WV4
Shape: Round, Flat, Square.
Size Range:
| |
Diameter(mm) |
Thickness (mm) |
Width (mm) |
Length(mm) |
| Round |
50-420 |
- |
- |
2000-5800 |
| Square |
50-420 |
- |
- |
2000-5800 |
| flat |
- |
20-50 |
80-600 |
2000-5800 |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details |
In seaworthy packing, as your requirement. |
| Delivery details |
within 30-50 days |
Chemical Composition:
| Grade |
C |
Mn |
P |
S |
Si |
Cr |
W |
V |
| 1.2516 |
1.15-1.25 |
0.20-
0.35 |
0.035 max |
0.035 max |
0.15-
0.30 |
0.15-0.25 |
0.90-
1.10 |
0.07
-0.12 |
Heat Treatment:
Soft annealing: Heat to 720-750oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230.
Stress relieving: Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening: Harden from a temperature of 760-820oC, 800-840oC followed by water or oil quenching. Hardness after quenching is 64-66 HRC.
TEMPERING: Tempering temperature: 150-250oC. See the data bellow.
Applications:
Twist drills and tapes, ejectors, punches, reamers, countersinks, engraving tools, metal cutting saws. Usually delivered as silver steel.
Introduction:
Low alloyed W cold working tool steel.