35nc6 Fe-Pl62 DIN1.5815 35nicr6 Steel

• Customization: Available
• Type: Round
• Standard: DIN
• Model NO.: 35NC6 FE-PL62 DIN1.5815 35NiCr6
• Composition: Ferrous Steel Scrap
• Technique: Hot Forged or Hot Rolled
• Shape: Round,Flat or Square
• Surface Treatment: Black Surface, Grinded,Peeled,Milled,Polished
• Special Use: Alloy Structural Steel
• Application: Structural Steel Bar
• Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
• Smelting Process: Ef, Eaf, ESR
• Delivery Condition: Hot Rolled, Forged, Annealed,Quenched and Tempered
• Surface Condition: Black Surface, Grinded,Peeled,Milled,Polished
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: CHENGQUAN
• Origin: Huangshi, Hubei
• HS Code: 7228600000
• Production Capacity: 5000tons/Year

Product Description

Description

Alloy special steel

Application

? Crankshafts.
? Shafts.
? Various gears.
? Fasteners etc
 

All Grades Comparison

DIN	EN	ANFOR	AECMA
1.5815	35NiCr6	35NC6	FE-PL62

Quality Standard

EN 10083 Steels for quenching and tempering. Technical delivery conditions for alloy steels
EN 10250 Open steel die forgings for general engineering purposes. Alloy special steels

Chemical Composition(%)

C	Mn	Si	P	S	Cr	Ni
0.30-0.37	0.60-0.90	0.40 max	0.025 max	0.025 max	0.80-1.10	1.20-1.60

Mechanical Properties(T=20°C if not differently stated)

Process	Diameter(mm)	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation A5 (%)	Area Reduction Ratio C (%)	Impact Value Kv (J) Room Temperature	Hardness (HB)
SOFT ANNEALED	/	/	/	/	/	/	223 max
QUENCHED AND TEMPERED	16 max	880-1080	740 min	12 min	40 min	/	261-318
QUENCHED AND TEMPERED	16-40	880-1080	740 min	12 min	40 min	35 min	261-318
QUENCHED AND TEMPERED	40-100	780-980	640 min	15 min	40 min	35 min	231-289

HEAT TREATMENT:

Process	TEMPERATURE °C	Cooling Medium
Hot plastic deformation	850-1100	/
Normalization	850-880	air
Soft annealing	640-690	air
Hardening	840-860	oil
Tempering	530-630	air

Mill′s test certificate:

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.