DIN1.7380 Stainless Steel for High Temperature

• Customization: Available
• Type: Stainless Steel Bars
• Standard: AISI, JIS, DIN
• Model NO.: DIN1.7380, 10CrMo9-10, ASTM A182, F22
• Grade: High Quality Steel
• Certification: ISO
• Shape: Round, Flat, Square.
• Technique: Forged. Rolled
• Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
• Size Range: 50-420mm
• Surface Condition: Black, Grinded, Peeled, Rough Turned, Polished
• Delivery Condition: Annealed, Quenched + Tempered
• Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
• MOQ: 1t
• Transport Package: Seaworthy Packing
• Specification: DIN1.7380, 10CrMo9-10, ASTM A182, F22
• Trademark: Chengquan
• Origin: Huangshi, China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

DIN1.7380 Stainless Steel for High Temperature

Similar Grade: DIN1.7380, 10CrMo9-10, ASTM A182, F22

Shape: Round, Flat, Square.

Size Range:

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	50-420	-	-	2000-5800
Square	50-420	-	-	2000-5800
flat	-	20-50	80-600	2000-5800

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Mechanical Properties:

Delivery Condition	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation(%)	Reduction Ratio(%)	Hardness (HB)
Normalized and Tempered	900 min	675 min	/	/	/
Slow Cooling	415 min	205 min	20 min	35 min	170 max

 
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:

Grade	C	Mn	P	S	Si	Cr	W	Cu
1.7380	0.05-0.15	0.30- 0.60	0.040 max	0.040 max	0.50 max	2.00- 2.50	0.87- 1.13	-

 
Heat Treatment:
Normalizing: Temperature: 920°-980°C.

Stress Relieving: Stree relieving to remove maching stresses should be carried out by heating to 675°C, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Austenizating: Temperature:920°-980°C

Tempering: Tempering temperature: 650°-750°C

Forging: Hot forming temperature: 850°-1050°C
Applications:
1.7380 stainless steel is a low alloy steel containing nominally 2.25% Chromium. This F22 stainless steel is widely used in the oil patch wellhead applications for connectors, hangers and block valves. Hardness levels up to 22 HRC are approved to NACE MR0175. The grade is often used as the base metal for clad components. If supplied to ASTM A182 in the normalised and tempered condition, the 0.2% Proof Stress minimum is 30 KSI.