AISI 4027 Alloy Steel with High Quality (UNS G40270)

• Customization: Available
• Type: Alloy Steel Bar
• Standard: ASTM
• Model NO.: 4027
• Composition: Ferrous Steel Scrap
• Technique: Hot Rolled, Forged
• Shape: Round, Square, Flat
• Surface Treatment: Grinded, Peeled, Polished, Rough Turned
• Special Use: Mold Steel
• Application: Tool Steel Bar
• Similar Grades: Uns G40270
• Size Range: Diameter: 20-480mm
• Quality Standard: ASTM-A29
• Delivery Condition: Annealed, Qunched and Tempered
• Surface Condition: Grinded, Peeled, Polished, Rough Turned
• Transport Package: Apply The Shipping Packing
• Specification: Diameter: 20-480mm
• Trademark: FUSHUN
• Origin: Hubei, Huangshi
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

Similar Grades:
UNS G40270
Shape: 
Round, Flat, Square.
Size Range:
 

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	20-480	-	-	2000-5800
Square	20-480	-	-	2000-5800
flat	-	20-50	80-600	2000-5800

 
Steel-making Condition: 
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

Chemical Composition(%)
 

C	Mn	P	S	Si	Cr	V	Mo	Ni
0.25-0.30	0.70-0.90	<=0.035	<=0.040	0.15-0.35	/	/	0.20-0.30	/

 

 
Mechanical Properties

Properties	Metric	Imperial
Tensile strength	515 MPa	74700 psi
Yield strength	325 MPa	47100 psi
Bulk modulus (typical for steel)	140 GPa	20300 ksi
Shear modulus (typical for steel)	80.0 GPa	11600 ksi
Elastic modulus	190-210 GPa	27557-30458 ksi
Poisson's ratio	0.27-0.30	0.27-0.30
Elongation at break (in 50 mm)	30.00%	30.00%
Reduction of area	52.90%	52.90%
Hardness, Brinell	143	143
Hardness, Knoop (converted from Brinell hardness)	163	163
Hardness, Rockwell B (converted from Brinell hardness)	78	78
Hardness, Vickers (converted from Brinell hardness)	149	149
Machinability (annealed and cold drawn. Based on 100 machinability for AISI 1212 steel)	70	70

 
 
 
 
 

Introduction:
Alloy steels are steels containing elements such as chromium, cobalt, nickel. When compared with carbon steels, the alloy steels are a lot more responsive to mechanical and heat treatments.
Alloy steels contain a variety of steels with compositions that exceed the limitations of Si, Va, Cr, Ni, Mo, Mn, B and C allocated for carbon steels. These steels are used in specific melting and deoxidization processes for particular kind of applications.