100crmn6 1.3520 Oil Hardening Tool Steel

• Customization: Available
• Type: Flat
• Standard: DIN, BS
• Model NO.: 100CrMn6 1.3520
• Composition: Ferrous Steel Scrap
• Technique: Hot Forged or Hot Rolled
• Shape: Round,Flat or Square
• Surface Treatment: Black Surface, Grinded,Peeled,Milled,Polished
• Special Use: Bearing Steel
• Application: Tool Steel Bar
• Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
• Smelting Process: Ef, Eaf, ESR
• Delivery Condition: Hot Rolled, Forged, Annealed,Quenched and Tempered
• Surface Condition: Black Surface, Grinded,Peeled,Milled,Polished
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: FUSHUN
• Origin: China
• HS Code: 7228600000
• Production Capacity: 5000tons/Year

Product Description

Introduction:

Medium alloy, oil hardening tool steel, which is hard-wearing.

Applications:

Roller bearings with thickness up to 50 mm.

Quality Standard:

DIN 17230-1980 Ball and Roller Bearing Steels

All Grades Comparison:

Material No.	EN
1.3520	100CrMn6

Chemical Composition(%)

C	Si	Mn	P	S	Cr	Ni	Cu
0.90-1.05	0.50-0.70	1.00-1.20	0.030 max	0.025 max	1.40-1.65	0.30 max	0.30 max

HEAT TREATMENT:

· NORMALIZING: Normalizing temperature: 860-900°C.
· SOFT ANNEALING: Heat to 760-800°C, cool slowly in furnace. This will produce a maximum Brinell hardness of 217.
· STRESS RELIEVING: Stress relieving to remove machining stresses should be carried out by heating to approx. 650°C, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
· HARDENING: Harden from a temperature of 830-890°C followed by oil quenching. Hardness after quenching is approx. 64 HRC.
· TEMPERING: Tempering temperature: 150-180°C.

Mill′s test certificate:

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.