1.5028,61SiCr7, ASTM9260, 60Si2Mn, JIS SUP6 Spring Steel (DIN17222)
Similar Grade: 1.5028,61SiCr7, ASTM9260, 60Si2Mn, JIS SUP6
Shape: Round, Flat, Square.
Size Range:
Frame
Processing
Shape |
Round |
Flat |
Square |
| Thickness |
Width |
Rolling |
12-130mm |
4-150mm |
100-900mm |
-
|
Forging |
50-1000mm |
70-800mm |
300-2000mm |
70-1000mm |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Cold Rolled only
Cold Rolled+Soft Annealed (G)
Cold Rolled+Soft Annealed+Cold Rolled (G+K)
Cold Rolled+Hardened+Tempered (H+A)
Surface Condition:
Grey Blue (GR)
Bright (BK)
Polished (P)
Polished and Colour Tempered (P+AF)
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details |
In seaworthy packing, as your requirement. |
| Delivery details |
within 20-50 days |
Chemical Composition:
| Grade |
C |
Mn |
Si |
P |
S |
Cr |
Ni |
Cu |
| 61SiCr7 |
0.56-
0.64 |
0.70-
1.00 |
1.50-
2.00 |
0.035 max |
0.035 max |
0.25 max |
0.25 max |
0.25 max |
Heat treatment:
Tensile Strength Rm (Mpa): 1275 min
Yield Strength Rp0.2 (Mpa): 1180 min
Elongation A5 (%): 5 min
Area Reduction Ratio C (%): 25 min
FORGING:Hot forming temperature: 1050-850ºC.
SOFT ANNEALING: Heat to 640-680ºC, cool slowly in furnace. This will produce a maximum Brinell hardness of 255.
HARDENING: Harden from a temperature of 830-860ºC followed by oil quenching.
TEMPERING:Tempering temperature: 350-550ºC, air.
Mill′s test certificate:
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
Application:
Spring Steel is typically used because of its' high yield strengths, resistance to deformation and its ability to return to its original shape.