DIN1.4462 UNS S32205 UNS S31803 F55 2205 Duplex Stainless Steel
Similar Grade: DIN1.4462, UNS S32205, UNS S31803, F55, 2205
Shape: Round, Flat, Square.
Size Range:
| |
Diameter(mm) |
Thickness (mm) |
Width (mm) |
Length(mm) |
| Round |
50-420 |
- |
- |
2000-5800 |
| Square |
50-420 |
- |
- |
2000-5800 |
| flat |
- |
20-50 |
80-600 |
2000-5800 |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details |
In seaworthy packing, as your requirement. |
| Delivery details |
within 30-50 days |
Chemical Composition:
| Grade |
C |
Mn |
P |
S |
Si |
Cr |
Ni |
Mo |
N |
| 1.4462 |
0.03 max |
2.0 max |
0.035 max |
0.035 max |
1.0 max |
21.0-
23.0 |
4.50-
6.50 |
2.50-
5.50 |
0.10-
0.22 |
Heat Treatment and Fabrication:
Hot Forming: Forming below 600°F is recommended whenever possible. When hot forming is required, the workpiece should be heated uniformly and worked in the range of 1750 to 2250°F. 2205 duplex stainless steel is quite soft at these temperatures and is readily formed. Above this range, 2205 duplex stainless steel is subject to hot tearing. Immediately below this range, the austenite becomes substantially stronger than the ferrite and may cause cracking, a particular danger to "cold" edges. Below 1700°F there can be rapid formation of intermetallic phases because of the combination of temperature and deformation. Whenever hot forming is done, it should be followed by a full solution anneal at 1900°F minimum and rapid quench to restore phase balance, toughness, and corrosion resistance. Stress relieving is not required or recommended; however, if it must be performed, the material should receive a full solution anneal at 1900°F minimum, followed by rapid cooling or water quenching.
Cold Forming: 1.4462 duplex stainless steel is readily sheared and cold formed on equipment suited to working stainless steels. However, because of the high strength and rapid work hardening of 2205 duplex stainless steel, forces substantially higher than those for austenitic steels are required to cold form it. Also because of the high strength, a somewhat larger allowance must be made for springback.
Heat Treatment: 1.4462 duplex stainless steel should be annealed at 1900°F minimum, followed by rapid cooling, ideally by water quenching. This treatment applies to both solution annealing and stress relieving. Stress relief treatments at any lower temperature carry the risk of precipitation of detrimental intermetallic or nonmetallic phases.
Applications:
Chemical processing, transport and storage - pressure vessels, tanks, piping, and heat exchangers
Oil and gas exploration and processing equipment - piping, tubing, and heat exchangers
Marine and other high chloride environments
Effluent scrubbing systems
Pulp and paper industry - digesters, bleaching equipment, and stock-handling systems
Cargo tanks for ships and trucks
Food processing equipment
Biofuels plants
Introduction:
1.4462 duplex stainless steel is a 22% Chromium, 3% Molybdenum, 5-6% Nickel nitrogen alloyed duplex stainless steel with high general, localized and stress corrosion resistance properties in addition to high strength and excellent impact toughness.
1.4462 duplex stainless steel provides pitting and crevice corrosion resistance superior to 316L or 317L austenitic stainless steels in almost all corrosive media. It also has high corrosion and erosion fatigue properties as well as lower thermal expansion and higher thermal conductivity than austenitic.
The yield strength is about twice that of austenitic stainless steels. This allows a designer to save weight and makes the alloy more cost competitive when compared to 316L or 317L.
1.4462 duplex stainless steel is particularly suitable for applications covering the -50F/+600F temperature range. Temperatures outside this range may be considered but need some restrictions, particularly for welded structures.