1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel

Product Details
Customization: Available
Type: Stainless Steel Bars
Standard: ASTM, AISI, GB, DIN, EN
Still deciding? Get samples of US$ 80/Piece
Request Sample
Manufacturer/Factory, Trading Company

360° Virtual Tour

Diamond Member Since 2022

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

to see all verified strength labels (14)
  • 1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel
  • 1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel
  • 1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel
  • 1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel
  • 1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel
  • 1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel
Find Similar Products

Basic Info.

Model NO.
1.4542 UNS S17400 630 17-4PH
Certification
ISO
Shape
Round,Flat or Square
Technique
Hot Rolled
Surface Treatment
Bright
Size Range
Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
Similar Grade
1.4542 Uns S17400 630 17-4pH
Delivery Condition
Hot Rolled, Forged, Annealed,Quenched and Tempered
MOQ
100kgs
Transport Package
Seaworth Packing
Specification
Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
Trademark
CHENGQUAN
Origin
Huangshi, Hubei
HS Code
7228100000
Production Capacity
5000tons/Year

Product Description

1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel
Similar Grade:

DIN
ASTM UNS CNU
1.4545 XM-12 S15500 15-5PH

Chemical Composition(%)

C
Si Mn P S Cr Ni Cu Nb+Ta
0.07 max 1.0 max 1.0 max 0.030 max 0.035 max 14.0-15.0 3.5-5.5 2.5-4.5 0.15-0.45

Mechanical Properties

Delivery Condition
Modulus of Elasticity
(GPa)
Modulus of Rigidity
(GPa)
Tensile Strength Rm (Mpa) Yield Strength Rp0.2(Mpa) Elongation % in 2″ (50.8 mm) Reduction Of Area
 (%)
Hardness
 (HRC)
A(annealed) / / / / / / 35 max
H 900 197.6 77.3 1378 min 1276 min 14 min 50 min 44 min
H925 / / 1309 min 1207 min 14 min 54 min 42 min
H1025 / 75.9 1173 min 1138 min 15 min 56 min 38 min
H1075 / 69 1138 min 1035 min 16 min 58 min 36 min
H1100 / / 1035 min 931 min 17 min 58 min 34 min
H1150 / 69 1000 min 862 min 19 min 60 min 33 min

Mill′s test certificate:
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
Quality Standard:
ASTM A564 2004 Standard Specification for Hot Rolled and Cold Finished Age Hardening Stainless Steel Bars and Shapes
ASTM A705 Standard Specification for Age Hardening Stainless Steel Forgings

Introduction:
15-5PH is a martensitic precipitation-hardening stainless steel that provides high strength, good
corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C) and good toughness in both the longitudinal and transverse directions in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling.
15-5PH is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in the
aerospace, chemical, petrochemical, food processing, paper and general metalworking industries.

Applications:
Aircraft components
High pressure corrosive fabricated parts such as valves
Shafts
Fasteners
Fittings and gears
 
 1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now
Contact Supplier