M2 High Speed Steel with High Quality (DIN 1.3343)

• Customization: Available
• Type: Alloy Steel Bar
• Standard: ASTM
• Model NO.: M2
• Composition: Ferrous Steel Scrap
• Technique: Hot Rolled, Forged
• Shape: Round, Square, Flat
• Surface Treatment: Black, Grinded, Peeled, Polished, Rough Turned
• Special Use: Mold Steel
• Application: Structural Steel Bar
• Similar Grades: DIN 1.3343
• Size Range: Diameter: 20-480mm
• Delivery Condition: Annealed, Qunched and Tempered
• Surface Condition: Annealed, Qunched and Tempered
• Quality Standard: ASTM -A600
• Transport Package: Apply The Shipping Packing
• Specification: Diameter: 20-480mm
• Trademark: FUSHUN
• Origin: Hubei, Huangshi
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

Similar Grades:
DIN1.3343

Shape: 
Round, Flat, Square.

Size Range:
 

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	20-480	-	-	2000-5800
Square	20-480	-	-	2000-5800
flat	-	20-50	80-600	2000-5800

 

Steel-making Condition: 
EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 

Chemical Composition:

C	Mn	P	S	Si	Cr	V	W
0.78-0.88	0.15-0.40	0.030max	0.030max	0.20-0.45	3.75-4.50	1.75-2.20	5.50-6.75

 
 

Machinability:

When properly annealed, M2 steel has a machinability rating of 65 percent when compared to a 1% Carbon Steel rated at 100.

Dimensional Stability:

When air quenched from the proper hardening temperature, this grade can be expected to expand approximately .001 in. per in. Note: Distortion (bending, bowing and twisting) and part geometry can add to the variations in movement of a part that is being hardened.

Thermal Cycling:

In order to avoid decarburization, this grade should be annealed and/or hardened in a controlled neutral atmosphere, vacuum, or neutral salt furnace environment.
1. Anneal: Heat to 1600° F, soak thoroughly at heat. Furnace cool 25° F per hour to 900° F, air cool to room temperature. Approximate annealed hardness 241 Maximum Brinell.
2. Stress Relief of Unhardened Material: Heat slowly to 1200 to 1250° F. Soak for two hours per inch of thickness at heat. Slow cool (furnace cool if possible) to room temperature.
3. Hardening:
a. Preheat: Heat slowly to 1550° F, soak thoroughly, heat to 1850° F, soak thoroughly.
b. Harden: Soak time in the furnace varies from a few minutes to a 15 minutes, depending tool size, heat capacity of the furnace, and the size of the charge.
- Heat to 2150 to 2200° F for max. toughness and minimum distortion.
- Heat to 2250 to 2275° F for max. hardness and abrasion resistance.
c. Quench: For full hardness, oil quench to 150-200° F. Air quench to 150° F. When quenching in hot salt maintain the quench just above the Ms temperature. After equalizing withdraw parts from the hot salt and air cooled to 150° F.
d. Temper: Double temper is mandatory, three tempers are sometimes preferred. Soak for 2 hours per inch of thickness. Air cool to room temperature between tempers. The best tempering range for hardness, strength and toughness is 1000 to 1050° F.

Introduction:

M2 steel is a general purpose molybdenum high speed steel. M2 steel is characterized by balanced combination of abrasion resistance, toughness and good red hardness. Due to its comparatively low carbon content, M2 steel has an excellent combination of toughness properties and abrasion resistance when properly hardened and tempered. M2 steel is used in a wide used for all kinds of cutting tool, knife and punch and die applications.

Applications:

M2 steel is a high speed steel suitable for cutting tools such as, twist drills, broaches, taps, milling cutters, reamers, saws, knives etc. In terms of performance, M2 steel is an all-round steel to be used in cutting conditions where demands for hot hardness are moderate. The term hot hardness is understood as the ability of the steel to retain its hardness even at elevated temperatures. M2 steel is also suitable for cold work applications, e.g. in tools for punching, forming and pressing, etc. The steel possesses an admirable combination of wear resistance and toughness and in these respects is superior to the high alloyed cold work steels.