1.3520 100crmn6 Oil Hardening Tool Steel
Product Details
| Customization: | Available |
|---|---|
| Type: | Round |
| Standard: | DIN, GB |
Diamond Member Since 2022
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
High Repeat Buyers Choice
Experienced Team
In-stock Capacity
Management Certification
More than 50% of buyers repeatedly choose the supplier
The supplier has 18 foreign trading staff(s) and 10 staff(s) with over 6 years of overseas trading experience
The supplier has In-stock capacity
The supplier has quality management system certification, including:
ISO9001:2015 certificate
ISO9001:2015 certificate
Sign In to see all verified strength labels (14)
Find Similar Products
Basic Info.
- Model NO.
- 1.3520 100CrMn6
- Composition
- Ferrous Steel Scrap
- Technique
- Forged, Rolled
- Shape
- Round, Flat, Square.
- Surface Treatment
- Black, Grinded, Peeled, Rough Turned, Polished
- Special Use
- Mold Steel
- Size Range
- 50-420mm
- Steel-Making Condition
- Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+ESR
- Delivery Condition
- Annealed, Quenched + Tempered
- Surface Condition
- Black, Grinded, Peeled, Rough Turned, Polished
- Transport Package
- Seaworthy Packing
- Specification
- 1.3520 100CrMn6
- Trademark
- FUSHUN
- Origin
- China
- HS Code
- 7228600000
- Production Capacity
- 500tons Per Month
Product Description
100CrMn6 1.3520 Oil Hardening Tool Steel
Similar Grade: 100CrMn6, 1.3520.
Shape: Round, Flat, Square.
Size Range:
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
Chemical Composition:
Heat Treatment:
Normalizing: Normalizing temperature: 860-900ºC
Soft Annealing: Heat to 760-800ºC, cool slowly in furnace. This will produce a maximum Brinell hardness of 217.
Stress Relieving: Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening: Harden from a temperature of 830-890ºC followed by oil quenching. Hardness after quenching is approx. 64 HRC.
TEMPERING: Tempering temperature: 150-180ºC.
Applications:
Roller bearings with thickness up to 50 mm.
Similar Grade: 100CrMn6, 1.3520.
Shape: Round, Flat, Square.
Size Range:
| Diameter(mm) | Thickness (mm) | Width (mm) | Length(mm) | |
| Round | 50-420 | - | - | 2000-5800 |
| Square | 50-420 | - | - | 2000-5800 |
| flat | - | 20-50 | 80-600 | 2000-5800 |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details | In seaworthy packing, as your requirement. |
| Delivery details | within 30-50 days |
Chemical Composition:
| Grade | C | Mn | P | S | Si | Cr | Ni | Cu |
| 1.3520 | 0.90-1.05 | 1.00-1.20 | 0.030 max | 0.025 max | 0.50-0.70 | 1.40-1.65 | 0.30 max | 0.30 max |
Heat Treatment:
Normalizing: Normalizing temperature: 860-900ºC
Soft Annealing: Heat to 760-800ºC, cool slowly in furnace. This will produce a maximum Brinell hardness of 217.
Stress Relieving: Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening: Harden from a temperature of 830-890ºC followed by oil quenching. Hardness after quenching is approx. 64 HRC.
TEMPERING: Tempering temperature: 150-180ºC.
Applications:
Roller bearings with thickness up to 50 mm.
){kind=link}
Send your message to this supplier
People who viewed this also viewed
Find Similar Products By Category
- Supplier Homepage
- Products
- Tool Steel
- 1.3520 100crmn6 Oil Hardening Tool Steel
Related Categories
Hot Searches
More