1.4406, AISI306LN, X2CrNiMoN17-11-2 Austenitic Stainless Steel (EN1008-3)
Similar Grade: 1.4406, AISI306LN, X2CrNiMoN17-11-2
Shape: Round, Flat, Square.
Size Range:
Frame
Processing
Shape |
Round |
Flat |
Square |
| Thickness |
Width |
Rolling |
12-130mm |
4-150mm |
100-900mm |
-
|
Forging |
50-1000mm |
70-800mm |
300-2000mm |
70-1000mm |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details |
In seaworthy packing, as your requirement. |
| Delivery details |
within 30-50 days |
Chemical Composition:
| Grade |
C |
Mn |
P |
S |
Si |
Cr |
Ni |
Mo |
| 1.4406 |
0.03max |
2.0 max |
0.045 max |
0.030
max |
1.0 max |
16.50-
18.50 |
10.0-
12.0 |
2.0-
2.50 |
Heat treatment:
Hardness: 250
Tensile strength: 580-800
Elongation after fracture:40
Application:
Annealing Quench annealing should be performed at 1030 - 1110°C and followed by rapid cooling in water or air. For Ti-stabilised grades, annealing temperatures above 1070ºC may impair the resistance to intergranular corrosion. Ti-stabilised grades may also be given a stabilising treatment at lower temperatures. However, temperatures below 980°C should only be used after due consideration of the intended service environment. In applications where high residual stresses cannot be accepted, stress relief treatment may be necessary. This can be performed by annealing as outlined above, but may also be performed at lower temperatures. Please contact Outokumpu Stainless for further information. Hardening These grades cannot be hardened by heat treatment. However, they can be hardened by cold working.