DIN1.4539 904L Stainless Steel with High Quality

• Customization: Available
• Type: Stainless Steel Bars
• Standard: ASTM
• Model NO.: DIN1.4539 904L
• Grade: DIN1.4539 904L
• Certification: ISO
• Shape: Round
• Technique: Hot Rolled
• Surface Treatment: Bright
• Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
• Similar Grade: DIN1.4539 904L
• Delivery Condition: Hot Rolled, Forged, Annealed,Quenched and Tempered
• MOQ: 500kgs
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: CHENGQUAN
• Origin: Huangshi, Hubei
• HS Code: 7228600000
• Production Capacity: 5000tons/Year

Product Description

Quality Standard
ASTM A182 Standard Specification for Forged or Rolled Alloy-Steel Pipe Flanges, Forged Fittings, and Valves and Parts
EN 10088 part3 stainless steel
All Grades Comparison

ASTM A182	EN10088
904L	1.4539

Chemical Composition(%)

Steel Grade	C	Si	Mn	P	S	Cr	Ni	Mo	Cu	N
904L	0.02 max	1.0 max	2.0 max	0.040 max	0.030 max	19.0-23.0	23.0-28.0	4.0-5.0	1.0-2.0	0.10 max
1.4539	0.02 max	0.7 max	2.0 max	0.040 max	0.010 max	19.0-21.0	24.0-26.0	4.0-5.0	1.2-2.0	0.15 max

Mechanical Properties (Annealed)

Hardness (HB)	Tensile Strength (Mpa)	Yield Strength (Mpa)	Elongation (%) (Long.)	Impact Value (J) (Long.)
230 max	530-730	230-260	35 min	100 min

Corrosion Resistance
Where a level of resistance to pitting corrosion better than 316 is required 904L stainless steel may be suitable. With its high nickel content at 25% it offers improved resistance to chloride stress corrosion cracking compared to other austenitic grades such as 304.

Welding
904L stainless steel can be welded using common fusion and resistance methods. A more highly alloyed filler is recommended to give the optimum corrosion properties in the weld. We recommend you contact your welding consumables supplier who should provide you full assistance and information on welding 904L stainless steel.

Mill′s test certificate
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.

Introduction
904L stainless steel combines molybdenum and copper with iron for tremendously increased resistance to reducing acids like sulphuric acid. It stands up extremely well to chlorides in the environment for low pitting and crevice corrosion, as well as stress corrosion cracking.

Applications
904L stainless steel is widely used in the chemical, pharmaceutical, oil and gas industries. Typical applications include tanks, valves, heat exchangers, flanges and manifolds. The addition of copper to the composition of 904L stainless steel aids its suitability for components such as tanks and other products used in handling sulphuric and phosphoric acid.